Has a great influence on the heat treatment after forging quality
We can provide free samples . Please contact Email for any inquiries
1) tissue defects some forging, can be improved in heat treatment after forging, microstructure and properties can still be obtained satisfactory final heat treatment after forging. For example, in structural steel forgings for general overheating in coarse grained and widmanstatten structure, hypereutectoid steel and bearing steel due to improper cooling slightly reticulate carbide.
2) tissue defects some forgings, eliminate the use of difficult to normal heat treatment by high temperature normalizing, normalizing, repeatedly, low temperature decomposition, high temperature diffusion annealing and other measures to improve. For example, coarse crystal, 9Cr18 stainless steel twin carbide.
3) tissue defects some forgings, general heat treatment process can not be eliminated, the result makes the final heat treatment after forging performance decline, not even qualified. For example, serious stone fracture and fracture of facet, burnt, stainless steel in the ferrite band, ledebrite high alloy tool steel in the carbide network and belt etc..
4) tissue defects some forgings, in the final heat treatment will be further development, even cause cracking. For example, coarse grain structure of alloy structure steel forgings, if the heat treatment after forging has not improved, in carbon, carbonitriding and quenching after often cause coarse and properties of martensite unqualified; coarse banded carbides in high speed steel, quenching is often caused by cracking. The common defects in the forging process and its causes in the second chapter, introduced in detail in this paper.