Effects of the imported bearing service life may be many factors may cause factors and internal friction sound has been further instructions, use. For the main factors is the adjustment of the installation, use and maintenance, maintenance and repair, etc. in accordance with the technical requirements. The imported bearing installation, use, maintenance, maintenance technology of Edabearing load, the speed of operation, the lubrication state monitoring and inspection, found that the direct reason for abnormal to normal adjustment.
Installation conditions, for one of the factors is often caused by bearing package status change between the various parts of the incorrect installation of the bearing capacity, the primary factor, the abnormal state of the operating temperature of the bearing Edavibration, noise, progressive, quality of raw material is improved. The proportion of raw materials quality factors of bearing failure analysis has dropped significantly, but it is still one of the main factors of bearing failure.
1 strict steel raw material inspection, prevent containing martensite, decarburization, surface roughness, surface striations and raw material breach defects into the drawing; or by pretreatment, improved material properties and processing.
2 preventing and improving work bad microstructure defect, such as coarse lamellar pearlite, ferrite net etc..
3 strict control of bearing steel metallurgy quality, prevent contain nonmetallic inclusions, folding defects blank into the processing flow, prevent the steel parts brittle failure.
Edabearing manufacturing through forging, heat treatment, machining, lubrication condition, the direct cause of abnormal to monitoring and inspection, adjustment back to normal.

Installation conditions is one of the factors bearing is the primary factor often cause packet state change between the various parts of the incorrect installation of the bearing force, not the normal operating state, and the main factors of the termination of the inner life, refers to the structural design, manufacturing process and material quality, three factors determine bearing quality. For the main factors is the adjustment of the installation, use and maintenance, maintenance and repair, etc. in accordance with the technical requirements. Installation conditions is to use one of the factors of rolling bearing is the most important factor is often caused by packet state change between the various parts of the incorrect installation of the bearing capacity, in the abnormal state of operation and early failure.
Installation conditions is to use one of the factors of rolling bearing is the most important factor is often caused by packet state change between the various parts of the incorrect installation of the bearing capacity, in the abnormal state of operation and early failure. According to the Edabearing installation, use, maintenance, maintenance of the technical requirements of rolling contact bearing load, operating speed, temperature, vibration, noise and the lubrication state monitoring and inspection, found abnormal immediately find reasons, adjusting to normal. Rolling bearing metallurgical quality of material is the impact of the main factors of early failure of rolling bearings.
With the progress of Metallurgical Technology (such as rolling bearing steel, vacuum degassing etc.), improving the quality of raw materials. With the progress of Metallurgical Technology (such as rolling bearing steel, vacuum degassing etc.), improving the quality of raw materials. The proportion of raw materials quality factors in fault analysis of rolling bearing has decreased significantly, but it is still one of the main factors of rolling bearing failure. The appropriate selection of rolling bearing fault should be considered.
Internal factors mainly refers to the structural design, manufacturing process and material quality, three factors determine the quality of the rolling bearing.
Firstly, the structure design and advanced at the same time, there will be a longer service life of rolling bearings. Rolling bearing manufacturing after forging, heat treatment, turning, grinding and assembly processes of operation. Treatment of advanced, rationality, stability will also affect the service life of rolling bearing. Influence of process of rolling bearing heat treatment and grinding, tend to have a more direct relationship related to the quality of the products and the fault of rolling bearing.
The main task of the Edabearing failure analysis is based on plenty of background material, analysis of data and failure mode, identify the main factors causing the rolling bearing failure, so that to improve the rolling bearing, prolong the service period, in order to avoid the early failure of rolling bearing beat all events.